Fiberglass roving for Filament winding

Short Description:

◎ Uniform tension and small drape

◎ Good wear resistance under high tension, good transition smoothness, good cluster extraction

◎ Excellent process performance, low retraction tension and good banding, less hairiness

◎ Rapid and complete infiltration, good bonding with various resins

◎ The electrical properties of the product are good, the mechanical strength of the product is excellent, and the fatigue resistance is good

◎ Excellent process performance, suitable for fast winding under high tension

◎ Excellent chemical corrosion resistance and aging resistance, such as H2S corrosion in oil and natural gas

◎ Excellent wear resistance

◎ High retention rate of boiled products


Product Detail

Product Tags

The product is an alkali-free twist-free roving. The surface of the roving is coated with silane-based sizing agent. It is compatible with unsaturated resin, epoxy resin and vinyl resin system. It can be used in amine or acid anhydride curing system and internal or external fade Type of winding process used.

The product has high mechanical strength, good electrical performance and good fatigue performance. It is mainly used in the manufacture of chemical storage tanks, reinforced thermoplastic pipes, high-tension winding process to produce small-diameter sucker rods, and winding high-pressure pipelines, pressure vessels, and high-pressure gas cylinders. , pultruded profiles, bars, boats, high-voltage fiberglass reinforced plastic pipes, hollow insulating sleeves, insulating tie rods and other ultra-high-voltage composite insulators, and are widely used in power generation, transmission and distribution and other power systems.

Roving-5

Product Specifications

Model Roving type Glass type Sizing type Typical filament diameter (um) Typical linear density (tex)
ER-266 Assembled Roving

E

Silane

13 2400
EDR-306B

Direct Roving

12 、13 735 、765
EDR-308 17 、21 1100、 2000
EDR-308H 17 、21、24 600、1200、2000、2400、4800
EDR-308S 17 、21 、24 600 / 900、2400 / 4800、2000、2400、4800
EDR-310S 15、17、24 1100、735 / 1200、2400
EDR-318 13、17、21、24 600、735、1200、1985、2100、2400、4800
EDR-386H 13、17、24、31 300、600、1200、2400、4800
EDR-386T 13、16、17、21、24、31 200、300、400、600、1200、2400、4800

Technical Parameters

Model Moisture content(%) Sizing content(%) Breakage strength(N/tex) Tensile strength(MPa) Tensile modulus(GPa) Shear strength(MPa)
ER-266 ≤ 0.07 0.55 ± 0.15 ≥ 0.40 / / /
EDR-306B

≤ 0.10

 

0.70 ± 0.10 ≥ 0.50 ( >12 um)
≥ 0.60 ( ≤ 12 um)
/ / /
EDR-308 0.60 ± 0.10 ≥ 0.40 2625.0 / 380.6 81.49 / 11.82 72.0 / 10.4
EDR-308H 0.55 ± 0.15 ≥ 0.40 2675 82.2 74
EDR-308S ≥0.40 (<4800tex)
≥ 0.35 ( ≥ 4800 tex)
2590 82.0 74.3
EDR-310S ≥ 0.40 2450 81.76 70.0
EDR-318 0.55 ± 0.10 ≥ 0.40 2530 81.14 70.0
EDR-386H 0.50 ± 0.15 ≥ 0.40 (<17 um)
≥ 0.35 (18~24 um)
≥ 0.30 ( >24 um)
2765 / 2682 81.76 / 81.47 /
EDR-386T 0.60 ± 0.10 ≥0.40 (≤2400 tex)
≥0.35 (2401~4800 tex)
≥0.30 (>4800 tex)
2660 / 2580 80.22 / 80.12 68.0

Instructions

◎The product is best used within one year after production, and should be stored in the original packaging before use, and ensure a cool and dry environment.

◎ Please avoid collision when using the product to prevent the yarn from being scratched or broken.

◎ Please pay attention to the temperature and humidity balance of the environment during storage, and can be adjusted appropriately when using.

◎ When using, please control the tension reasonably and ensure the uniformity of tension, so as to achieve the best effect of the product.

SMC

Packaging

Products are packaged in pallet + cardboard and shrink film

Storage

Under normal circumstances, fiberglass products should be stored in a dry, cool and moisture-proof environment. The best temperature and humidity in the environment should be kept at -10℃~35℃ and ≤80% respectively. For safety and to avoid product damage, pallets should not be stacked more than three layers high. When overlapping pallets, special care should be taken to move the upper pallets correctly and smoothly to prevent product from collapsing and causing losses.


  • Previous:
  • Next: